Abstract
Iron granular films were synthesized in silicone polymers by implantation of 40 keV Fe+ ions with a fluence of 1.25 · 1017 ion/cm2 into viscous polymer substrates with various viscosity of 20–1000 Pa s. After the implantation the
iron-implanted silicone substrates have been cured in the solid rubber-like state on the expiration of 72 h. The influence of the substrate viscosity on the magnetic properties of the synthesized iron films was studied by ferromagnetic resonance (FMR) spectroscopy. It was shown that magnetic anisotropy and magnetization of the iron granular films is strongly and non-monotonically depended on the viscosity of silicone polymer under irradiation. Particularly, the
maximal value of magnetization, 610 G, is observed for iron granular film synthesized at substrate viscosity on order of 70 Pa s. This value is higher than the magnetization of films obtained in silicone substrate implanted with iron ions in fully cured state.
iron-implanted silicone substrates have been cured in the solid rubber-like state on the expiration of 72 h. The influence of the substrate viscosity on the magnetic properties of the synthesized iron films was studied by ferromagnetic resonance (FMR) spectroscopy. It was shown that magnetic anisotropy and magnetization of the iron granular films is strongly and non-monotonically depended on the viscosity of silicone polymer under irradiation. Particularly, the
maximal value of magnetization, 610 G, is observed for iron granular film synthesized at substrate viscosity on order of 70 Pa s. This value is higher than the magnetization of films obtained in silicone substrate implanted with iron ions in fully cured state.
Originalsprog | Engelsk |
---|---|
Tidsskrift | Nuclear Instruments and Methods in Physics Reseach B |
Vol/bind | 206 |
Sider (fra-til) | 1115-1119 |
Antal sider | 5 |
ISSN | 0168-583X |
Status | Udgivet - maj 2003 |
Udgivet eksternt | Ja |
Begivenhed | 13th International Conference on Ion Beam Modification of Materials - Kobe, Japan Varighed: 1 sep. 2002 → 6 sep. 2002 |
Konference
Konference | 13th International Conference on Ion Beam Modification of Materials |
---|---|
Land/Område | Japan |
By | Kobe |
Periode | 01/09/2002 → 06/09/2002 |