Influence of the glass-calcium carbonate mixture's characteristics on the foaming process and the properties of the foam glass

Publikation: Bidrag til tidsskriftTidsskriftartikelpeer review

65 Citationer (Scopus)

Abstrakt

We prepared foam glasses from cathode-ray-tube panel glass and CaCO3 as a foaming agent. We investigated the influences of powder preparation, CaCO3 concentration and foaming temperature and time on the density, porosity and homogeneity of the foam glasses. The results show that the decomposition kinetics of CaCO3 has a strong influence on the foaming process. The decomposition temperature can be modified by varying the milling time of the glass–CaCO3 mixture and thus for a specific CaCO3 concentration an optimum milling time exists, at which a minimum in density and a homogeneous closed porosity are obtained. Under the optimum preparation conditions the samples exhibit a density of 260 kg/m3. The thermal conductivity of the foam glass was measured to be 50–53 mW/(m K). The observed dependence of the foaming process on the decomposition kinetics of the foaming agent can be applied as a universal rule for foaming processes based on thermal decomposition.

OriginalsprogEngelsk
TidsskriftJournal of the European Ceramic Society
Vol/bind34
Udgave nummer6
Sider (fra-til)1591-1598
Antal sider8
ISSN0955-2219
DOI
StatusUdgivet - 2014

Fingeraftryk

Dyk ned i forskningsemnerne om 'Influence of the glass-calcium carbonate mixture's characteristics on the foaming process and the properties of the foam glass'. Sammen danner de et unikt fingeraftryk.

Citationsformater